Articles liés à Development of Nano-Ceramic Dispersed Cu-based Metal...
Development of Nano-Ceramic Dispersed Cu-based Metal Matrix Composites: Nano ceramic oxide dispersed metal matrix composite for electrical contacts - Couverture souple
L'édition de cet ISBN n'est malheureusement plus disponible.
Afficher les exemplaires de cette édition ISBN
Présentation de l'éditeur :
CuCr and CuCrAg alloys, with or without nanocrystalline Al2O3/ZrO2 dispersion, have been synthesized by mechanical alloying/milling. The milled powders were consolidated by conventional cold compaction and sintering, laser sintering, ECAP and high pressure sintering. Microstructural characterization evidence that milled product is Cu- rich extended solid solution with nanometric (< 50 nm) crystallite size with nano-alumina particles embedded in it. However, the microscopic and diffraction analysis of sintered products suggest that the alloyed matrix undergoes significant grain growth after sintering while the dispersoids retain their ultrafine size. Among all four consolidation methods high pressure sintering produces compacts of highest density, and mechanical and electrical properties. 10 wt % Al2O3 dispersed Cu-4.5Cr-3Ag alloy consolidated by high pressure sintering at 800oC shows the maximum hardness (435 VHN) and wear resistance. The electrical conductivity of the pellets without and with nano-Al2O3 dispersion is about 40-45 % IACS(international annealing copper standard) and 35 %IACS, respectively.
Biographie de l'auteur :
The author was born on November 22, 1981. He had graduated in Metallurgical and Materials Engineering from Bengal Engineering College Shibpur in 2002 and obtained M.S. in Engineering in 2005 from Department of Metallurgical and Materials Engineering, IIT Kharagpur. He completed his doctoral study from the same institute in 2010.
Les informations fournies dans la section « A propos du livre » peuvent faire référence à une autre édition de ce titre.
- ÉditeurLAP Lambert Academic Publishing
- Date d'édition2010
- ISBN 10 3843363110
- ISBN 13 9783843363112
- ReliureBroché
- Nombre de pages192
Acheter neuf
En savoir plus sur cette édition
EUR 71,02
Frais de port :
EUR 11,68
De Royaume-Uni vers Etats-Unis
Meilleurs résultats de recherche sur AbeBooks
Image d'archives
Development of Nano-Ceramic Dispersed Cu-Based Metal Matrix Composites
Edité par
LAP Lambert Academic Publishing
(2010)
ISBN 10 : 3843363110
ISBN 13 : 9783843363112
Neuf
Couverture souple
Quantité disponible : > 20
Vendeur :
Evaluation vendeur
Description du livre Etat : New. PRINT ON DEMAND Book; New; Fast Shipping from the UK. No. book. N° de réf. du vendeur ria9783843363112_lsuk
Acheter neuf
EUR 71,02
Autre devise
Image d'archives
Development of Nano-Ceramic Dispersed Cu-based Metal Matrix Composites: Nano ceramic oxide dispersed metal matrix composite for electrical contacts
Edité par
LAP LAMBERT Academic Publishing
(2010)
ISBN 10 : 3843363110
ISBN 13 : 9783843363112
Neuf
Couverture souple
Quantité disponible : > 20
Vendeur :
Evaluation vendeur
Description du livre Etat : New. N° de réf. du vendeur ABLING22Oct2817100612188
Acheter neuf
EUR 81,36
Autre devise
Image d'archives
Development of Nano-Ceramic Dispersed Cu-Based Metal Matrix Composites
Edité par
LAP Lambert Academic Publishing 2010-10
(2010)
ISBN 10 : 3843363110
ISBN 13 : 9783843363112
Neuf
PF
Quantité disponible : 10
Vendeur :
Evaluation vendeur
Description du livre PF. Etat : New. N° de réf. du vendeur 6666-IUK-9783843363112
Acheter neuf
EUR 68,30
Autre devise
Image fournie par le vendeur
Development of Nano-Ceramic Dispersed Cu-based Metal Matrix Composites
Edité par
LAP LAMBERT Academic Publishing Okt 2010
(2010)
ISBN 10 : 3843363110
ISBN 13 : 9783843363112
Neuf
Taschenbuch
Quantité disponible : 2
Vendeur :
Evaluation vendeur
Description du livre Taschenbuch. Etat : Neu. This item is printed on demand - it takes 3-4 days longer - Neuware -CuCr and CuCrAg alloys, with or without nanocrystalline Al2O3/ZrO2 dispersion, have been synthesized by mechanical alloying/milling. The milled powders were consolidated by conventional cold compaction and sintering, laser sintering, ECAP and high pressure sintering. Microstructural characterization evidence that milled product is Cu- rich extended solid solution with nanometric (< 50 nm) crystallite size with nano-alumina particles embedded in it. However, the microscopic and diffraction analysis of sintered products suggest that the alloyed matrix undergoes significant grain growth after sintering while the dispersoids retain their ultrafine size. Among all four consolidation methods high pressure sintering produces compacts of highest density, and mechanical and electrical properties. 10 wt % Al2O3 dispersed Cu-4.5Cr-3Ag alloy consolidated by high pressure sintering at 800oC shows the maximum hardness (435 VHN) and wear resistance. The electrical conductivity of the pellets without and with nano-Al2O3 dispersion is about 40-45 % IACS(international annealing copper standard) and 35 %IACS, respectively. 192 pp. Englisch. N° de réf. du vendeur 9783843363112
Acheter neuf
EUR 68
Autre devise
Image d'archives
Development of NanoCeramic Dispersed Cubased Metal Matrix Composites Nano ceramic oxide dispersed metal matrix composite for electrical contacts
Edité par
LAP LAMBERT Academic Publishing
(2010)
ISBN 10 : 3843363110
ISBN 13 : 9783843363112
Neuf
PAP
Quantité disponible : > 20
Vendeur :
Evaluation vendeur
Description du livre PAP. Etat : New. New Book. Shipped from UK. THIS BOOK IS PRINTED ON DEMAND. Established seller since 2000. N° de réf. du vendeur L0-9783843363112
Acheter neuf
EUR 97,28
Autre devise
Image fournie par le vendeur
Development of Nano-Ceramic Dispersed Cu-based Metal Matrix Composites : Nano ceramic oxide dispersed metal matrix composite for electrical contacts
Edité par
LAP LAMBERT Academic Publishing
(2010)
ISBN 10 : 3843363110
ISBN 13 : 9783843363112
Neuf
Taschenbuch
Quantité disponible : 1
Vendeur :
Evaluation vendeur
Description du livre Taschenbuch. Etat : Neu. nach der Bestellung gedruckt Neuware - Printed after ordering - CuCr and CuCrAg alloys, with or without nanocrystalline Al2O3/ZrO2 dispersion, have been synthesized by mechanical alloying/milling. The milled powders were consolidated by conventional cold compaction and sintering, laser sintering, ECAP and high pressure sintering. Microstructural characterization evidence that milled product is Cu- rich extended solid solution with nanometric (< 50 nm) crystallite size with nano-alumina particles embedded in it. However, the microscopic and diffraction analysis of sintered products suggest that the alloyed matrix undergoes significant grain growth after sintering while the dispersoids retain their ultrafine size. Among all four consolidation methods high pressure sintering produces compacts of highest density, and mechanical and electrical properties. 10 wt % Al2O3 dispersed Cu-4.5Cr-3Ag alloy consolidated by high pressure sintering at 800oC shows the maximum hardness (435 VHN) and wear resistance. The electrical conductivity of the pellets without and with nano-Al2O3 dispersion is about 40-45 % IACS(international annealing copper standard) and 35 %IACS, respectively. N° de réf. du vendeur 9783843363112
Acheter neuf
EUR 68
Autre devise
Image d'archives
Development of NanoCeramic Dispersed Cubased Metal Matrix Composites Nano ceramic oxide dispersed metal matrix composite for electrical contacts
Edité par
LAP LAMBERT Academic Publishing
(2010)
ISBN 10 : 3843363110
ISBN 13 : 9783843363112
Neuf
PAP
Quantité disponible : > 20
Vendeur :
Evaluation vendeur
Description du livre PAP. Etat : New. New Book. Delivered from our UK warehouse in 4 to 14 business days. THIS BOOK IS PRINTED ON DEMAND. Established seller since 2000. N° de réf. du vendeur L0-9783843363112
Acheter neuf
EUR 74,87
Autre devise
Image d'archives
Development of Nano-Ceramic Dispersed Cu-based Metal Matrix Composites: Nano ceramic oxide dispersed metal matrix composite for electrical contacts
Edité par
LAP LAMBERT Academic Publishing
(2010)
ISBN 10 : 3843363110
ISBN 13 : 9783843363112
Neuf
Couverture souple
Quantité disponible : 5
Vendeur :
Evaluation vendeur
Description du livre N° de réf. du vendeur STOCK12829143
Acheter neuf
EUR 105,27
Autre devise