Etat : New. Dieser Artikel ist ein Print on Demand Artikel und wird nach Ihrer Bestellung fuer Sie gedruckt. Strontium silicate (Sr2SiO4) nanophosphors were prepared by solution combustion synthesis method were characterised by X-ray diffraction, SEM and TEM. Structural optimisation of Sr2SiO4 nanophosphors were done by variation in temperature, fuel and calcinati. N� de r�f. du vendeur 1396902957

Contacter le vendeur

Acheter neuf

EUR 37,23

Autre devise

Frais de port : EUR 9,70

De Allemagne vers France

Destinations, frais et d�lais

Quantit� disponible : Plus de 20 disponibles

Ajouter au panier

Image d'archives

Structural characterization and analysis of Sr2SiO4 Nanophosphors

Manjunath C

Edit� par LAP LAMBERT Academic Publishing Jan 2024, 2024

ISBN 10 : 6207460014 ISBN 13 : 9786207460014

Neuf Taschenbuch

impression � la demande

Vendeur : BuchWeltWeit Ludwig Meier e.K., Bergisch Gladbach, Allemagne

�valuation du vendeur 5 sur 5 �toiles

Taschenbuch. Etat : Neu. This item is printed on demand - it takes 3-4 days longer - Neuware 68 pp. Englisch. N� de r�f. du vendeur 9786207460014

Contacter le vendeur

Acheter neuf

EUR 43,90

Autre devise

Frais de port : EUR 11

De Allemagne vers France

Destinations, frais et d�lais

Quantit� disponible : 2 disponible(s)

Ajouter au panier

Image fournie par le vendeur

Structural characterization and analysis of Sr2SiO4 Nanophosphors : Exploring the Structural Properties of Sr2SiO4 Nanophosphors: A Comprehensive Investigation

Manjunath C

Edit� par LAP LAMBERT Academic Publishing

ISBN 10 : 6207460014 ISBN 13 : 9786207460014

Neuf Taschenbuch

impression � la demande

Vendeur : AHA-BUCH GmbH, Einbeck, Allemagne

�valuation du vendeur 5 sur 5 �toiles

Taschenbuch. Etat : Neu. nach der Bestellung gedruckt Neuware - Printed after ordering - Strontium silicate (Sr2SiO4) nanophosphors were prepared by solution combustion synthesis method were characterised by X-ray diffraction, SEM and TEM. Structural optimisation of Sr2SiO4 nanophosphors were done by variation in temperature, fuel and calcination temperature and for the synthesis was obtained. The optimal condition for phosphor synthesised using glycine as a fuel calcinated at 900� C for the duration of 3 hours exhibited better crystallinity. The optimal condition was used further in synthesising of Sr2SiO4:Sm3+, Sr2SiO4:Eu3+ and Sr2SiO4:Dy3+ phosphors. XRD of all the synthesised phosphors were well indexed with JCPDS card No.39-1256 that corresponds to orthorhombic structure. Scherrer and WH-plots were used to determine the average crystallite size and were found to be around 40 nm, 43 nm and 38 nm for Sm3+, Eu3+ and Dy3+ doped Sr2SiO4 respectively. Detailed structural analysis of Dy3+ doped Sr2SiO4 was studied. N� de r�f. du vendeur 9786207460014

Contacter le vendeur

Acheter neuf

EUR 44,59

Autre devise

Frais de port : EUR 10,99

De Allemagne vers France

Destinations, frais et d�lais

Quantit� disponible : 1 disponible(s)

Ajouter au panier

Image fournie par le vendeur

Structural characterization and analysis of Sr2SiO4 Nanophosphors

Manjunath C

Edit� par LAP LAMBERT Academic Publishing Jan 2024, 2024

ISBN 10 : 6207460014 ISBN 13 : 9786207460014

Neuf Taschenbuch

Vendeur : buchversandmimpf2000, Emtmannsberg, BAYE, Allemagne

�valuation du vendeur 5 sur 5 �toiles

Taschenbuch. Etat : Neu. Neuware -Strontium silicate (Sr2SiO4) nanophosphors were prepared by solution combustion synthesis method were characterised by X-ray diffraction, SEM and TEM. Structural optimisation of Sr2SiO4 nanophosphors were done by variation in temperature, fuel and calcination temperature and for the synthesis was obtained. The optimal condition for phosphor synthesised using glycine as a fuel calcinated at 900� C for the duration of 3 hours exhibited better crystallinity. The optimal condition was used further in synthesising of Sr2SiO4:Sm3+, Sr2SiO4:Eu3+ and Sr2SiO4:Dy3+ phosphors. XRD of all the synthesised phosphors were well indexed with JCPDS card No.39-1256 that corresponds to orthorhombic structure. Scherrer and WH-plots were used to determine the average crystallite size and were found to be around 40 nm, 43 nm and 38 nm for Sm3+, Eu3+ and Dy3+ doped Sr2SiO4 respectively. Detailed structural analysis of Dy3+ doped Sr2SiO4 was studied.Books on Demand GmbH, �berseering 33, 22297 Hamburg 68 pp. Englisch. N� de r�f. du vendeur 9786207460014