ISBN: 9786202207621 - lithium-ion conductors based on mil-121 metal organic frameworks: a developing field of solid state electrolytes (8 résultats)

Etat : New. pp. 84.

Paperback. Etat : Brand New. 84 pages. 8.66x5.91x0.19 inches. In Stock.

Etat : New.

Taschenbuch. Etat : Neu. This item is printed on demand - it takes 3-4 days longer - Neuware -This work was aimed to investigate a new type of solid state lithium (Li) ion conductor as electrolyte for all solid-state Li-ion batteries. A metal organic framework (MOF) MIL-121 was modified in two different ways in order to become Li-ion conductive. The post synthetic modifications (PSM) were lithiation with lithium acetate (LiAc) and lithium hydroxide (LiOH) as well as esterification of the carboxylic groups of MIL-121 with methanol (MeOH), ethanol (EtOH) and isopropanol. After PSM the porous samples were soaked with different liquids like common liquid electrolytes, which leads to a decreased activation energy of Li-ion jumps in the crystal lattice meaning an increased Li-ion conductivity of the material. Esterified MIL-121 was soaked with ionic liquids containing lithium bis(trifluoromethane)sulfonimide (LiTFSI), because the introduction of Li-ions to the structure was necessary. 84 pp. Englisch.…

Etat : New. Print on Demand pp. 84.

Etat : New. PRINT ON DEMAND pp. 84.

Taschenbuch. Etat : Neu. nach der Bestellung gedruckt Neuware - Printed after ordering - This work was aimed to investigate a new type of solid state lithium (Li) ion conductor as electrolyte for all solid-state Li-ion batteries. A metal organic framework (MOF) MIL-121 was modified in two different ways in order to become Li-ion conductive. The post synthetic modifications (PSM) were lithiation with lithium acetate (LiAc) and lithium hydroxide (LiOH) as well as esterification of the carboxylic groups of MIL-121 with methanol (MeOH), ethanol (EtOH) and isopropanol. After PSM the porous samples were soaked with different liquids like common liquid electrolytes, which leads to a decreased activation energy of Li-ion jumps in the crystal lattice meaning an increased Li-ion conductivity of the material. Esterified MIL-121 was soaked with ionic liquids containing lithium bis(trifluoromethane)sulfonimide (LiTFSI), because the introduction of Li-ions to the structure was necessary.…

Taschenbuch. Etat : Neu. This item is printed on demand - Print on Demand Titel. Neuware -This work was aimed to investigate a new type of solid state lithium (Li) ion conductor as electrolyte for all solid-state Li-ion batteries. A metal organic framework (MOF) MIL-121 was modified in two different ways in order to become Li-ion conductive. The post synthetic modifications (PSM) were lithiation with lithium acetate (LiAc) and lithium hydroxide (LiOH) as well as esterification of the carboxylic groups of MIL-121 with methanol (MeOH), ethanol (EtOH) and isopropanol. After PSM the porous samples were soaked with different liquids like common liquid electrolytes, which leads to a decreased activation energy of Li-ion jumps in the crystal lattice meaning an increased Li-ion conductivity of the material. Esterified MIL-121 was soaked with ionic liquids containing lithium bis(trifluoromethane)sulfonimide (LiTFSI), because the introduction of Li-ions to the structure was necessary.VDM Verlag, Dudweiler Landstraße 99, 66123 Saarbrücken 84 pp. Englisch.…