Solid state refrigeration potential par patel satyanarayan (8 résultats)

Etat : New.

Taschenbuch. Etat : Neu. Solid State Refrigeration Potential in Lead-free Ferroelectric Ceramic | Investigation of Solid State Refrigeration Potential in Ba0.85Ca0.15Zr0.1Ti0.9O3-based Ferroelectric Ceramics | Satyanarayan Patel | Taschenbuch | Englisch | 2022 | LAP LAMBERT Academic Publishing | EAN 9786204982298 | Verantwortliche Person für die EU: SIA OmniScriptum Publishing, Brivibas Gatve 197, 1039 RIGA, LETTLAND, customerservice[at]vdm-vsg[dot]de | Anbieter: preigu.…

Taschenbuch. Etat : Neu. This item is printed on demand - it takes 3-4 days longer - Neuware -This book attempts to shed light on the use of various physical and chemical routes towards the systematic investigation of exploring and enhancing (electro) caloric effects in bulk lead-free Ba0.85Ca0.15Zr0.1Ti0.9O3(BCZT) ceramics composition. Caloric effects were estimated by indirect predictions using Maxwell's relations in conjunction with experimental data. Electrocaloric(EC) effect in BCZT, Ba0.85Ca0.15Zr0.1Ti0.9-xFexO3 and Ba0.85Sr0.15Ti0.9Zr0.1O3(BSTZ) are found as 0.41K (0-21.5kV/cm), 0.86K (0-37kV/cm) and 2.4K at 303K (0-37kV/cm), respectively. Further, Ba0.85Ca0.075Sr0.075Ti0.9Zr0.1O3(BCSTZ) exhibits temperature invariant performance in spanning 60K (303K-363K). The BCSTZ and BSTZ ceramics have an improved electrocaloric behavior (1.5±0.1K and 2.4K) at an optimum sintering temperature of 1475°C and 1450°C for dwell time of 5hr and 4hr, respectively. A remarkably large elastocaloric response (DeltaTmax of 1.55K) is observed in BCZT at 340K. Finally, a novel cycle was proposed for suitably combining the multicaloric response using the same material. Additionally, inverse piezocaloric, flexocaloric and barocaloric effect in BCZT, (Ba0.67Sr0.37)TiO3, and PVDF was observed. 216 pp. Englisch.…

Etat : New. Dieser Artikel ist ein Print on Demand Artikel und wird nach Ihrer Bestellung fuer Sie gedruckt. This book attempts to shed light on the use of various physical and chemical routes towards the systematic investigation of exploring and enhancing (electro) caloric effects in bulk lead-free Ba0.85Ca0.15Zr0.1Ti0.9O3(BCZT) ceramics composition. Caloric effe.…

Etat : New. Print on Demand.

Taschenbuch. Etat : Neu. nach der Bestellung gedruckt Neuware - Printed after ordering - This book attempts to shed light on the use of various physical and chemical routes towards the systematic investigation of exploring and enhancing (electro) caloric effects in bulk lead-free Ba0.85Ca0.15Zr0.1Ti0.9O3(BCZT) ceramics composition. Caloric effects were estimated by indirect predictions using Maxwell's relations in conjunction with experimental data. Electrocaloric(EC) effect in BCZT, Ba0.85Ca0.15Zr0.1Ti0.9-xFexO3 and Ba0.85Sr0.15Ti0.9Zr0.1O3(BSTZ) are found as 0.41K (0-21.5kV/cm), 0.86K (0-37kV/cm) and 2.4K at 303K (0-37kV/cm), respectively. Further, Ba0.85Ca0.075Sr0.075Ti0.9Zr0.1O3(BCSTZ) exhibits temperature invariant performance in spanning 60K (303K-363K). The BCSTZ and BSTZ ceramics have an improved electrocaloric behavior (1.5±0.1K and 2.4K) at an optimum sintering temperature of 1475°C and 1450°C for dwell time of 5hr and 4hr, respectively. A remarkably large elastocaloric response (DeltaTmax of 1.55K) is observed in BCZT at 340K. Finally, a novel cycle was proposed for suitably combining the multicaloric response using the same material. Additionally, inverse piezocaloric, flexocaloric and barocaloric effect in BCZT, (Ba0.67Sr0.37)TiO3, and PVDF was observed.…

Etat : New. PRINT ON DEMAND.

Taschenbuch. Etat : Neu. This item is printed on demand - Print on Demand Titel. Neuware -This book attempts to shed light on the use of various physical and chemical routes towards the systematic investigation of exploring and enhancing (electro) caloric effects in bulk lead-free Ba0.85Ca0.15Zr0.1Ti0.9O3(BCZT) ceramics composition. Caloric effects were estimated by indirect predictions using Maxwell's relations in conjunction with experimental data. Electrocaloric(EC) effect in BCZT, Ba0.85Ca0.15Zr0.1Ti0.9-xFexO3 and Ba0.85Sr0.15Ti0.9Zr0.1O3(BSTZ) are found as 0.41K (0-21.5kV/cm), 0.86K (0-37kV/cm) and 2.4K at 303K (0-37kV/cm), respectively. Further, Ba0.85Ca0.075Sr0.075Ti0.9Zr0.1O3(BCSTZ) exhibits temperature invariant performance in spanning 60K (303K-363K). The BCSTZ and BSTZ ceramics have an improved electrocaloric behavior (1.5±0.1K and 2.4K) at an optimum sintering temperature of 1475°C and 1450°C for dwell time of 5hr and 4hr, respectively. A remarkably large elastocaloric response (¿Tmax of 1.55K) is observed in BCZT at 340K. Finally, a novel cycle was proposed for suitably combining the multicaloric response using the same material. Additionally, inverse piezocaloric, flexocaloric and barocaloric effect in BCZT, (Ba0.67Sr0.37)TiO3, and PVDF was observed.VDM Verlag, Dudweiler Landstraße 99, 66123 Saarbrücken 216 pp. Englisch.…